Yugal Plywoods are manufactured with high density core and face which are treated with Anti termite additives and are further bonded with in-house specially manufactured Phenol Formaldehyde BWP Grade resin, which is Eco-Friendly and non-hazardous to human and animal. It comes with double pressed thick face on both sides. Moreover, the finished plywood is subjected to proper chemical treatment with water soluble fixed type preservatives under vacuum pressure to ensure protection against wood destroying organisms and to make the product borer/termite proof and fungi free. Our ply woods go through seven step rigorous testing to make it dimensionally stable and anti warp in both dry and humid conditions.
Yugal 710 Marine Grade Plywood
| Technical Specifications IS 710 | ||
| Test | ISI Requirement | Results |
| Moisture content | 5% – 15% | 12% |
| Glue shear strength in dry condition | a. Individual Min. 1100 Newton, b. Average 1350 Newton. | a. 1550 Newton b. 1700 Newton |
| Glue shear strength | a. Individual Min. 800 Newton, b. Average 1000 Newton | a. 1300 Newton b. 1225 Newton |
| Glue Shear Strength in mycological test | a. Individual Min. 800 Newton, b. Average 1000 Newton. | a. 960 Newton b. 1200 Newton |
| Tensile Strength: a. Parallel to grain direction b. Right angle to grain direction c. Sum of both directions | a. Min. 420 Kgf./cm2 b. Min. 250 Kgf./cm2 c. Min. 845 Kgf./cm2 | a. 540 Kgf./cm2 b. 370 Kgf./cm2 c. 910 Kgf./cm2 |
Yugal 303 MR Grade Plywood
| Grade | MOE{N/mm2} | MOR{N/mm2} | ||
| Average | Min. Ind. | Average | Min. Ind. | |
| BWR Grade a. Along {direction parallel to the grain direction of the face veneer} b. Across {direction perpendicular to the grain direction of the face veneer} | a. 5000 b. 2500 | a. 4500 b. 2200 | a. 40 b. 20 | a. 36 b. 1 |
| MR Grade a. Along {direction parallel to the grain direction of the face veneer} b. Across {direction perpendicular to the grain direction of the face veneer} | a. 4000 b. 2000 | a. 3600 b. 1800 | a. 30 b. 15 | a. 27 b. 13 |